Octupolar molecules used as organic semiconductors

ABSTRACT

In the case of the materials according to the invention, the charge carrier mobility in the correspondingly prepared films is achieved if the molecules are composed in such a way that side chains—consisting of conjugated aromatic or heteroaromatic systems—are attached in direct conjugation to a central aromatic or heteroaromatic ring so that the total molecule acquires an octupolar structure. This octupolar structure permits an effective π-π interaction of the molecules with one another in a manner such that stacking of a plurality of molecules along an imaginary axis (central ring) can take place and various stacks from among these stacks can interact with one another by intermeshing of the side chains. The electronic properties of the materials are determined both by the arrangement of the molecules in a layer and by the molecular design. The type of side chains and of the central ring which is electronically coupled to the side chains and ideally reinforces the effects in comparison with side chains considered in isolation is important for this purpose.

The present invention relates to novel octupolar compounds and their preparation and use as organic semiconductors and in particular for organic field effect transistors.

The mobilities of charge carriers in organic semiconductors are at present not more than 1-2 cm²/Vs. The maximum operating frequency of transistors and hence of the electronic switching is limited by the mobility of the charge carriers (holes or electrons). Although mobilities of the order of magnitude of 10⁰ cm²/Vs are sufficient for driver application in the production of TFT active matrix displays, high-frequency applications are generally excluded.

For technical reasons, wireless information transmission (RF-ID systems) can be effected only above a certain minimum frequency. In systems which are supplied directly from the alternating electromagnetic field and hence also have no independent voltage supply, the carrier frequencies 125 kHz and 13.56 MHz are widely used. Fields of use are identification and marking technology (smart cards, ident tags (bar code replacement), electronic postage stamps, etc.).

On the one hand, products which contain a silicon-based chip are too expensive for many applications. For example, a silicon-based ident tag is not suitable for marking foods (price, expiry date, etc.).

On the other hand, polymers or organic semiconductors have the potential that cheap printing techniques can be used for their structuring and application.

However, the mobilities of the charge carriers in these materials are too low for the applications discussed above.

Processes for applying the semiconducting molecules (for example pentacene, oligothiophenes) in a manner which is as ordered as possible, for example by vacuum sublimation, have been developed. Ordered deposition of the organic semiconductor leads to an increase in the crystallinity of the semiconductor material and, owing to an improved π-π overlap between the molecules or the side chains, reduces the energy barrier [1]. These are substantially molecules having a linear structure.

Substitution of the semiconducting molecular units by bulky groups leads to the formation of liquid crystalline-like domains in the deposition of the organic semiconductor from the liquid or gas phase [2].

In the area of polymers, synthesis processes in which as high a regioregularity as possible is achieved by the use of asymmetric monomers have been developed [3].

In [4], various octupolar oligothienyl compounds are described. However, these have only a relatively low charge carrier mobility, in order to enable them to be advantageously used as organic semiconductors and are for the most part irreversibly oxidizable or reducible.

Kotha et al., Synlett 1999, No. 10, 1621-1623, disclose octupolar molecules based on benzene having short thiophene side chains.

In this invention, novel compounds for uses as organic semiconductors are described. The molecular structure of these compounds permits high mobility of the charge carriers in correspondingly prepared films.

1. According to claim 1, octupolar compounds of the following general formula are provided, the octupolar molecule being present in the form of stacks or molecular clusters:

-   -   in which X is CH or N;     -   in which Y is CH or N;     -   in which Z is O, S or N—R, in which R may be H, alkyl or aryl;     -   in which n is 2-6;     -   in which m is 0-6;     -   R₁ is n-alkyl, sec-alkyl, tert-alkyl, fluoroalkyl and/or         perfluoroalkyl;     -   R₂ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl,         fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl,         alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy         and/or perfluoroaryloxy;     -   R₃ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl,         fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl,         alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy         and/or perfluoroaryloxy.

In a preferred embodiment of the invention, m is 0, so that the compound according to the invention is composed of a central benzene or triazine and five-membered unsaturated rings in the side chains.

It is furthermore preferred if n is 3-6. This is particularly preferred if m is 0.

If m is not 0, m is preferably 2-6, more preferably 3-6.

In a preferred embodiment, Z is S. This is the case both if m is 0 and if m is not 0. For Z=N—R and R=alkyl, R preferably has 1-18 C atoms, more preferably 2-8 C atoms. R may be n-alkyl, sec-alkyl, tert-alkyl and/or cycloalkyl, n-alkyl being preferred. Examples are methyl, ethyl, butyl, propyl, pentyl, hexyl, heptyl, octyl, nonyl or decyl, in each case preferably as n-alkyls.

According to the invention, X is CH or N. Both possibilities are equally suitable for the compounds of the present invention.

According to the invention, Y may likewise be CH or N, both possibilities being equally suitable according to the invention.

In the compounds according to the invention, the radical R₁ is present on the carbon atom neighboring the group Z. This is important in order for the compounds according to the invention to be stable and reversibly oxidizable and therefore to be more suitable for use as organic semiconductors.

If R₁ is n-alkyl, sec-alkyl, tert-alkyl, fluoroalkyl or perfluoroalkyl, the number of C atoms in the alkyl chain is preferably 1-18 C atoms, more preferably 2-8 carbon atoms.

The radicals according to the invention for R₁ can preferably be partly fluorinated or perfluorinated, i.e. completely fluorinated. Perfluorination is preferred. According to the invention, fluorination is to be understood as meaning that H atoms have been replaced by one or more fluorine radicals.

In a particularly preferred embodiment, R₁ is an n-alkyl, n-fluoroalkyl and/or n-perfluoroalkyl radical. Here, it is particularly preferred if R₁ has 1-18, preferably 2-8, carbon atoms. It is also particularly preferred if R₁ is an ethyl and/or hexyl radical. If R₁ is one of said alkyl, n-alkyl, fluoroalkyl, n-fluoroalkyl, perfluoroalkyl and/or n-perfluoroalkyl radicals, the compounds according to the invention are more stable and better reversibly oxidizable. With regard to the use for organic field effect transistors, particularly good results were obtained with such compounds. In these cases, the organization of the molecules after application to a substrate is presumably better, so that better charge carrier mobility is achieved. This is not the case, for example, if R₁ is H, halogen or S-alkyl; according to the invention, the radicals H, halogen or S-alkyl are therefore not provided for R₁.

With regard to the preferred embodiments, R₂ is defined as follows for n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl, fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl, alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy and perfluoroaryloxy:

If R₂ is n-alkyl, sec-alkyl, tert-alkyl, O-alkyl (alkoxy), fluoroalkyl, perfluoroalkyl, alkynyl, alkylthiol or alkylnitrile, the number of C atoms in the alkyl chain is preferably 1-18 C atoms, more preferably 2-8 carbon atoms.

For R₂=cycloalkyl, cycloalkyl radicals having 4-6 C atoms are preferred, more preferably having 5-6 C atoms, which in each case may also be partly fluorinated or perfluorinated.

If R₂ is an aryl radical, O-aryl radical or S-aryl radical, six-membered aryl radicals, such as phenyl, thiophenyl or pyridyl radicals are preferred, which may also be partly fluorinated or perfluorinated. Regarding O-aryl and S-aryl, O-phenyl and S-phenyl are preferred, which may also be partly fluorinated or perfluorinated.

It is particularly preferable if R₂ is an H, alkyl, fluoroalkyl and/or perfluoroalkyl radical.

It is furthermore preferred if R₂ is an n-alkyl, n-fluoroalkyl and/or n-perfluoroalkyl radical.

In these cases, R₂ preferably has 1-18 carbon atoms, more preferably 2-8 carbon atoms.

For R₂=halogen, the halogen radical may be Cl, Br and/or I. Preferred halides are Br and I.

With regard to n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl, fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroalkyl, alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy and perfluoroaryloxy, R₃ is defined in the same way as R₂, also with regard to the preferred embodiments of R₁. In a preferred embodiment, however, R₃ is H. In the present invention, on the basis of the present state of knowledge, the chemical nature of the radical R₃ is less critical than the radicals R₁ and R₂, in particular R₁.

For R₃=halogen, the halogen radical may be Cl, Br and/or I. Preferred halides are Br and I.

Particularly preferably, the radicals R₂ and/or R₃ are an H or a short-chain alkyl group, such as methyl and/or ethyl.

The following compounds have proven to be particularly preferred for the present invention:

-   1,3,5-Tris[5-(5″-ethyl)-2,2′:5′,2″-terthiophenyl]-benzene -   1,3,5-Tris[5-(5′-hexyl)-2,2′-biphenyl]benzene -   1,3,5-Tris[-(5′″-ethyl)-2,2′:5′,2″:5″,2′″-quart-thiophene]benzene -   2,4,6-Tris[5-(5′-ethyl)-2,2′-biphenyl]-1,3,5-triazine -   2,4,6-Tris[5-(5″-ethyl)-2,2′:5′,2″-terthiophenyl]-1,3,5-triazine

The octopular molecules of the present invention are present in the form of stacks or molecular clusters. In this form, they can interact with one another intramolecularly and transfer charges with high mobility.

According to the present invention, it is possible to use, as organic semiconductors, compounds of the following formula, the octupolar molecules being present in the form of stacks or molecular clusters:

-   -   in which Y is CH or N;     -   in which Z is O, S or N—R, in which R may be H, alkyl or aryl;     -   in which n is 2-6;     -   in which m is 0-6;     -   R₁, is n-alkyl, sec-alkyl, tert-alkyl, fluoroalkyl and/or         perfluoroalkyl;     -   R₂ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl,         fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl,         alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy         and/or perfluoroaryloxy;     -   R₃ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl,         fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl,         alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy         and/or perfluoroaryloxy.

Regarding further embodiments and preferred uses, the radicals X, Y, Z, n, m, R₁, R₂ and R₃ are defined as above.

Use both as p-semiconductors and as n-semiconductors is preferred. These compounds can preferably be used in transistors, preferably in field effect transistors.

The compounds according to the invention can be prepared by known processes, as described, for example, in reference [4] (triketolization and dehydration of three equivalents of acetyl-aromatic molecules with tetrachlorosilane/ethanol (1:1)), [5] (aryl-aryl coupling) and [6] (aryl-aryl coupling). Triazine compounds according to the invention can be prepared, for example, by nucleophilic substitution of the corresponding lithium salts with cyanuric chloride.

In the present invention, reference is made to the following figures.

FIG. 1 a schematically shows a compound according to the invention, in which the side chains are represented by rectangles.

FIG. 1 b schematically shows a stack of a plurality of the molecules shown in FIG. 1 a and possible routes for intermolecular charge transport and intramolecular interaction routes between different molecular moieties.

FIG. 2 schematically shows intermolecular interactions between different stacks of molecules.

FIG. 3 a shows a family of output characteristics of a transistor of the compound 4, processed according to example 9.

FIG. 3 b shows transmission characteristics of a transistor of the compound 4, processed according to example 9.

DETAILED DESCRIPTION

In the case of the materials according to the invention, the charge carrier mobility in the correspondingly prepared films is achieved if the molecules are composed in such a way that side chains—consisting of conjugated aromatic or heteroaromatic systems—are attached in direct conjugation to a central aromatic or heteroaromatic ring so that the total molecule acquires an octupolar structure. This octupolar structure permits an effective π-π interaction of the molecules with one another in a manner such that stacking of a plurality of molecules along an imaginary axis (central ring) can take place and various stacks from among these stacks can interact with one another by intermeshing of the side chains. The electronic properties of the materials are determined both by the arrangement of the molecules in a layer and by the molecular design. The type of side chains and of the central ring which is electronically coupled to the side chains and ideally reinforces the effects in comparison with side chains considered in isolation is important for this purpose.

The compounds of the present invention have various advantages:

-   1. The mobility of the charge carrier is considerably improved in     relation to comparable side chains considered in isolation. -   2. Owing to their structure, the materials are readily soluble in     conventional solvents and are therefore suitable for economical     application techniques, such as printing, coating, etc. -   3. The materials can alternatively also be vaporized. -   4. The synthesis of the materials is comparatively simple. -   5. It is possible to prepare materials having a large structural     variation. -   6. Both p-semiconductors and n-semiconductors can be prepared.

The compounds of the present invention can be used as organic semiconductors, use as n- and p-semiconductors being possible. In particular, the compounds of the present invention can be used in electronic components, such as transistors, preferably field effect transistors. Particularly suitable potential applications are identification and marking chips in smart cards, and ident tags (as bar code replacement).

The materials according to the invention are distinguished by a high mobility of the charge carriers in a correspondingly prepared film. This is due to the structure of the compounds according to the invention and their arrangement relative to one another in a layer, which ideally represents stacking of the molecules, the individual molecules interacting electronically with their neighbors in the stack (cf. FIG. 1 b). This interaction is substantially more effective in the case of this class of molecule than in the case of comparable linear organic semiconductors, unless these have a monocrystalline structure. Furthermore, the electronic interaction of the individual molecular fragments (central ring, side chains) with one another ensures an enlargement of the π-system of the molecule, with the effect that high mobilities can be achieved with relatively short side chains, which can be obtained chemically substantially more simply and more economically, than with the molecules which are obtainable from a linear linkage of two comparable side chain fragments.

The effective interaction of different stacks or molecular clusters with one another (intermeshing—FIG. 2) permits good charge transport by transmission of the charge from one stack to another. Thus, the charge transport can also be effected over relatively long distances (1-100 μm), as are usual as gate lengths in organic field effect transistors without direct conjugation by means of chemical bonding as in conjugated polymers being necessary.

The invention is explained in more detail below with reference to examples, which, however, do not limit the scope of the invention.

EXAMPLES Example 1 1,3,5-Tris[5-(5″-ethyl)-2,2′:5′,2″-terthiophenyl]benzene (1)

Compound (1) can be prepared by at least two alternative routes:

-   a) Trimerization of 2-acetyl-(5″-ethyl)-2,2′:5′,2″-terthiophene by     means of silicon tetrachloride in toluene/EtOH as a solvent,     analogously to reference [4] -   b) Aryl-aryl coupling of 1,3,5-tris[2-(5-bromo)-thiophenyl]benzene     [4] with 2-tributylstannyl-(5′-ethyl)-2,2′-bithiophene by means of a     Pd⁰ catalyst in THF, analogously to reference [5].

In both cases, purification is effected by column chromatography over silica gel using n-hexane/CH₂Cl₂ (1:1) as an eluent (Rf=0.8) to give the same product. ¹H-NMR (CDCl3): δ [ppm]=1.33 (9H, t, CH₃); 2.83 (6H, q, CH₂); 6.70 (6H, dd, CH, J₁=3.5 Hz, J₂=1.1 Hz); 6.99 (6H, d, CH, J=3.6 Hz); 7.01 (6H, d, CH, J=4 Hz); 7.11 (6H, d, CH, J=4 Hz); 7.16 (6H, d, CH, J=3.6 Hz); 7.33 (6H, d, CH, J=4 Hz); 7.67 (3H, s, CH)

Example 2 (comparative example) 1,3,5-Tris[5-(2,2′-bithienyl)]benzene (2)

Compound (2) was prepared according to the literature method [4] and corresponds to one of the compounds disclosed there. The purification was effected by column chromatography using n-hexane/CH₂Cl₂ as an eluent (Rf=0.9). m.p.=135° C. (reference [4]=136° C.)

Example 3 1,3,5-Tris[5-(5′-hexyl)-2,2′-bithienyl]-benzene (3)

Compound (3) can be prepared by at least two alternative routes:

-   a) Trimerization of 2-acetyl-(5′-hexyl)-2,2′-bithiophene by means of     silicon tetrachloride in toluene/EtOH as a solvent, analogously to     reference [4] b) Aryl-aryl coupling of 1,3,5-tris     [2-(5-bromo)-thiophene]benzene [4] with     2-[(5-hexylthienyl)]magnesium bromide by means of an Ni^(II)     catalyst in THF, analogous to reference [6].

In both cases, the purification is effected by column chromatography over silica gel using n-hexane/CH₂Cl₂ (4:1) as an eluent (Rf=0.6) to give the same product.

¹H-NMR (CDCl3): δ [ppm]=0.88 (9H, t, CH₃); 1.30-1.36 (18H, m, CH₂); 1.66 (6H, tt, CH₂); 2.77 (6H, t, CH₂); 6.69 (6H, dd, CH, J₁=3.6 Hz, J₂=1.2 Hz); 7.04 (6H, d, J=3.8 Hz, CH), 7.18 (6H, d, J−3.9 Hz, CH), 7.23 (6H, d, J=3.9 Hz, CH); 7.31 (6H, d, J=3.8 Hz, CH); 7.69 (3H, s, CH).

Example 4 1,3,5-Tris[-(5′″-ethyl)-2,2′:5′,2″:5″,2′″-quartthiophenyl]benzene [4]

Compound (4) was by aryl-aryl coupling of 1,3,5-tris[2-(5-bromo)thiophenyl]benzene [4] with 2-tributylstannyl-(5″-ethyl)-2,2′:5′,2″-terthiophene by means of a Pd⁰ catalyst in THF, analogously to reference [5].

The purification is effected by column chromatography over silica gel using n-hexane/CH₂Cl₂ (1:1) as eluent (Rf=0.8).

¹H-NMR (CDCl3): δ [ppm]=1.35 (9H, t, CH₃); 2.84 (6H, q, CH₂); 6.81 (6H, dd, CH, J₁=3.4 Hz, J₂=1.2 Hz); 6.98 (6H, d, J=3.6 Hz), CH); 7.01 (6H, d, J=3.9 Hz, CH); 7.03 (6H, d, J=3.9 Hz, CH); 7.05 (6H, d, J=3.9 Hz, CH); 7.16 (6H, d, J=3.8 Hz, CH); 7.25 (6H, d, J=3.9 Hz, CH); 7.34 (6H, d, J=3.9 Hz, CH); 7.69 (3H, s, CH).

Example 5 2,4,6-Tris-[5-(5′-ethyl)-2,2′-bithienyl]-1,3,5-triazine (5)

Compound (5) was prepared by nucleophilic aromatic substitution of 2-[(5′-ethyl)-2,2′-bithienyl]lithium salt with cyanuric chloride in THF. The purification is effected by column chromatography over silica gel using n-hexane/CH₂Cl₂ (1:1) as an eluent (Rf=0.8).

Example 6 2,4,6-Tris-[5-(5″-ethyl)-2,2′:5′,2″-terthiophenyl]-1,3-triazine (6)

Compound (6) was prepared by nucleophilic aromatic substitution of 2-[(5″-ethyl)-2,2′:5′,2″-terthienyl]-lithium salt with cyanuric chloride in THF. The purification is effected by column chromatography over silica gel using n-hexane/CH₂Cl₂ (1:1) as an eluent (Rf=0.75).

Example 7 Preparation of a Substrate Solution

In principle, all organic solvents whose boiling point is lower than the decomposition temperature of the compounds 1-6 and in which these have a solubility of at least 0.1 percent by mass, e.g. chloroform, dichloromethane, THF, acetone, cyclohexanone, ethyl acetate, toluene, cresol, γ-butyrolactone, NMP and DMF, are suitable as solvents for the layer preparation.

100 mg of a compound described under examples 1-6 were dissolved in 10 g of chloroform by shaking the mixture of the two components in a closed sample tube on a mechanical shaker for 1 hour. The solution was then rendered particle-free by means of pressure filtration into a steam-cleaned sample tube (filter size 0.2 μm).

Example 8 Film Preparation (Spin Coating Technique)

A solution prepared as under example 7 was applied by spin coating (1000-5000 rpm, 20 s, nitrogen atmosphere) to a suitable substrate on which transistors and/or circuit structures had been defined beforehand (e.g. Si wafer, glass or flexible film). The substrate was then dried for 2 minutes at 80° C. under inert gas.

Example 9 Film Preparation (Vapor Deposition)

A compound (examples 1-6) was applied to a substrate, as under example 15, under a high vacuum (10⁻⁶ to 10⁻⁷ mmHg) by means of an evaporator. Here, the vaporization times and substrate temperatures depended on the properties of the compounds and the desired layer thickness.

Example 10 Film Preparation (Printing)

A solution prepared as under example 7 and comprising corresponding additives is printed on a suitable substrate by means of a suitable screen in a screen printing machine and then dried at 80° C.

Example 11 Measurement of the Charge Carrier Mobilities

A field effect transistor processed as under examples 8-10 and consisting of gate electrode, gate dielectric and metal or polymer source and drain contacts is contacted on an analytical sampler by means of metal tips. Using an electrical parameter measuring apparatus (e.g. Agilent 4156), a transistor characteristic is measured. The charge carrier mobility is calculated from the characteristics. For compounds of examples 1-6, charge carrier mobilities are about 10⁻² to more than 10⁻¹ cm²/Vs were determined and are shown in table 1. TABLE 1 Charge carrier mobilities of examples 1-6. Film Film Compound preparation μ[cm²/Vs] preparation μ[cm²/Vs] 1 Ex. 8 0.04 Ex. 9 0.3 2 Ex. 8 0.0005 Ex. 9 0.006 3 Ex. 8 0.02 Ex. 9 0.1 4 Ex. 8 0.05 Ex. 9 0.4 5 Ex. 8 0.01 Ex. 9 0.09 6 Ex. 8 0.05 Ex. 9 0.15

Table 1 shows that the charge carrier mobility of compound (2) is substantially lower than that of the compounds according to the invention. Moreover, it was observed that field effect transistors and other “devices” degrade within hours and have only low redox stability, whereas the field effect transistors and devices with the compounds according to the invention are stable for weeks.

Example 12

In order to demonstrate the suitability, according to the invention, of octupolar compounds where m is not equal to 0, the experiments described above for determining the charge carrier mobility were repeated on field effect transistors comprising the following model compounds, the film preparation having been effected according to example 9:

Dec-5T-dec (linear compound comprising decyl, 5 thiophene rings and decyl in this sequence):

Dec-2T-Ph-2T-dec (linear compound comprising decyl, 2 thiophene rings, phenyl, 2 thiophene rings, decyl in this sequence):

The following results were obtained: μ [cm²/Vs] Dec-5T-dec: 0.5 Dec-2T-Ph-2T-dec: 0.3

It was thus possible to show that, using conjugation via phenyl rings does not adversely affect the charge carrier mobility in transistors compared with corresponding compounds having a thiophene instead of the phenyl ring.

REFERENCES

-   [1] D. J. Gundlach, C. C. Kuo, S. F. Nelson and T. N. Jackson 57th     Annual Device Research Conference Digest, pages 164-165, June     1999 H. E. Katz et al. Nature, Vol. 404, 2000, 478. -   [2] P. Bäuerle et al, Synthetic Metals, 101, 1999, 544; Adv. Mater.     4, 1992, 102. -   [3] Z Boa et al, Macromol. Symp. 2000, 1180. M. M. Bouman et al,     Adv. Mater. 7, 1995, 385. -   [4] F. Cherioux et al. Adv. Funct. Mater. 11/4, 2001, 305-309. -   [5] H. E. Katz et al, Chem. Mater. 10, 1998, 457-459. -   [6] R. D. McCullough et al, J. Org. Chem. 58, 1993, 904-912. 

1. An octupolar compound of the following general formula, the octupolar molecule being present in the form of stacks or molecular clusters:

in which X is CH or N; in which Y is CH or N; in which Z is O, S or N—R, in which R may be H, alkyl or aryl; in which n is 2-6; in which m is 0-6; R₁ is n-alkyl, sec-alkyl, tert-alkyl, fluoroalkyl and/or perfluoroalkyl; R₂ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl, fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl, alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy and/or perfluoroaryloxy; R₃ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl, fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl, alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy and/or perfluoroaryloxy.
 2. The compound as claimed in claim 1, wherein m is
 0. 3. The compound as claimed in claim 1, wherein n=3-6.
 4. The compound as claimed in claim 1, wherein Z is S.
 5. The compound as claimed in claim 1, wherein R₁ is an n-alkyl, n-fluoroalkyl and/or n-perfluoroalkyl radical.
 6. The compound as claimed in claim 5, wherein R₁ has 1-18, preferably 2-8, carbon atoms.
 7. The compound as claimed in claim 1, wherein R₂ is an H, alkyl, fluoroalkyl and/or perfluoroalkyl radical.
 8. The compound as claimed in claim 1, wherein R₂ is an n-alkyl, n-fluoroalkyl and/or n-perfluoroalkyl radical.
 9. The compound as claimed in claim 1, wherein R₂ has 1-18 carbon atoms, preferably 2-8 carbon atoms.
 10. The compound as claimed in claim 1, selected from the following group: 1,3,5-Tris[5-(5″-ethyl)-2,2′:5′,2″-terthiophenyl]benzene

1,3,5-Tris[5-(5′-hexhyl)-2,2′-bithienyl]benzene

1,3,5-Tris[-(5′″-ethyl)-2,2′:5′,2″:5″,2′″-quartthiophenyl]benzene

2,4,6-Tris[5-(5′-ethyl)-2,2′-biphenyl]1,3,5-triazine

2,4,6-Tris[5-(5″-ethyl)-2,2′:5′,2″-terthiophenyl]-1,3,5-triazine


11. The use of octupolar compounds of the following general formula, the octupolar compounds being present in the form of stacks or molecular clusters:

in which X is CH or N; in which Y is CH or N; in which Z is O, S or N—R, in which R may be H, alkyl or aryl; in which n is 2-6; in which m is 0-6; R₁ is n-alkyl, sec-alkyl, tert-alkyl, fluoroalkyl and/or perfluoroalkyl; R₂ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl, fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl, alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy, perfluoroaryloxy; R₃ is H, halogen, n-alkyl, sec-alkyl, tert-alkyl, cycloalkyl, fluoroalkyl, perfluoroalkyl, aryl, fluoroaryl, perfluoroaryl, alkoxy, fluoroalkoxy, aryloxy, fluoroaryloxy, perfluoroalkoxy, perfluoroaryloxy, as organic semiconductors.
 12. The use as claimed in claim 11, wherein the semiconductor is a p-semiconductor or n-semiconductor.
 13. The use as claimed in claim 11 in transistors.
 14. The use as claimed in claim 13 in field effect transistors. 